Lamberts manufactures cast glass which is glass formed by rolling processes. The company uses state-of-the-art machinery and complies with the highest quality and environmental standards. Lamberts fabricates all glasses according to a unique EcoGlass concept and is one of the leading factories of high-quality architectural glass with the lowest CO2 emissions.
LINIT U-Glass from Lamberts is an alkali-lime glass. It's a special form of cast glass consisting mainly of sand, lime, soda, and dolomite. These raw materials are carefully melted down in a cast glass furnace. The glass strip taken from the oven is bent into a U-shape whilst still in its plastic phase when it is then cooled and hardened. After the closely monitored cooling process, the desired lengths are automatically cut, checked for quality, and packaged in batches in transport foil.
Surfaces
504 | Clarissimo | Cord |
| | |
Ice | Magico | Moiré |
| | |
Prismasolar | Solar | |
| | |
Dimensions
LINIT U-Glass can be mounted in considerable lengths (up to 7 meters depending on the wind load) without any intermediate support. Thanks to its high static strength, side braces usually are not necessary, resulting in a facade with a maximum of glass and a minimum of frame profiles.
LINIT U-profiled glass is supplied from 100 cm up to a maximum length of 700 cm depending on the type. Within this range, fixed dimensions can be ordered to any desired length considering the production tolerances.
Sandblasted Process
LINIT S is a U-profiled glass with a sandblasted inner surface refracting and diffusing the light completely. As a result, outlines can no longer be seen clearly in contrast to directed permeability. This creates a soft, whitish hue making the LINIT facade more attractive and providing additional lightness at low costs, especially when the glass facade is backlit.
All LINIT glasses except the coated glasses 1.7W, azure, and solex, can be sandblasted up to a length of 7 meters. If desired, it is also possible to only partially sandblast the LINIT glasses to create translucent surfaces within the glass wall.
LINIT Low Iron
This product is a premium U-profiled glass. Due to its optimized low-iron raw material composition, LINIT low iron has a high light-transmission factor of approx. 90%, as well as a higher radiation-transmission factor of approx. 88% (usual production tolerances must be taken into account). It is significantly brighter and less green than the glass melt of standard production.